re HT 1080/15n20
hey guys to I have a small piece of Damascus that I made a long time ago and it been just sittin around so I decided to do something with its made from 1084 and 15n20 so I cant remember if I hted it I dint think I did actually but when I was drilling a hole in the tang (so I could loop a wire in it for part of the ht ) it seemed hard to drill Not quite as hard as I would suspect as if I had HT ed it but it was harder than "soft stocksteel" so I thought maybe it could have hardened a lil bit in the process of forge weling the billet togathe BUT I am not positive it was a while ago so maybe I did ht it either way I want to ht it again just so I KNOW I did it so I know with other steels you would have to go through all the annealing stages before re thing but for some reason I THINK I remember someone saying with 1084 you don't neec to do the annealing as its a forgiving steel so I remember right?? or do I have to anneal it?
|
10-21-2016, 01:10 PM
|
Skilled
|
|
Join Date: Jul 2013
Location: NE Tennessee
Posts: 409
|
|
get you some carbide drill bits already, and you wont have to worry about this... youll just be able to drill the hole and keep going.
run a file across it and thatll tell you if its hardened or not.
or just send the steel to one of us, (with return shipping) and we will check it out and tell you if its hardened or not.
|
10-21-2016, 01:30 PM
|
Guru
|
|
Join Date: Aug 2015
Location: ny
Posts: 1,438
|
|
damon...I have carbide drills...what happened was since I don't remember hThing it I went to drill the hole (I use this hole after it comes out of oil and goes into liquicd nitrogen I slip a wire through it so I can hang the blade in the dewar) so thinking this steel was soft I went to drill that hole with a regular bit (like I do when ever its soft no need for carbide reg. bit will go right through) the regular bit started no problem then bogged down like the steel was hard. so I took a carbide bit and finished the hole but the carbide bit went though much easier and quicker than usually if its hard. AND yes I did check it with a file and between what the file did and what the drill bits did I came to the conclusion (as I said ) that its deffinitly harder than "soft" steel is but not as hard as I think it should be if HTed ANYWAy point is I think the steel is slightly hard but not as hard as I would like it and no I don't need some one else to tell me if its hard or not that was not the question the question was if I HT it again do I have to anneal it... if it was 440c or cpms35vn yeh deffintily anneal but I remember hearing that 1084 doesn't always need to be annealed
|
10-21-2016, 01:55 PM
|
Skilled
|
|
Join Date: Mar 2012
Location: Alabama
Posts: 554
|
|
Just normalize it and it will be fine. Did you make the billet? If so how many layers? How much time did you spend welding it? Sometimes if one takes too much time or folds too many times you can get appreciable carbon loss, I doubt that's the problem. Just normalize and re try your heat treat.
|
10-21-2016, 02:45 PM
|
Guru
|
|
Join Date: Aug 2015
Location: ny
Posts: 1,438
|
|
alright thanks JM that is what I needed to know. yes I made the billet as I said it was a while ago I don't remer how long it took me to do and its a very low layer count I was going for a bold pattern cant remember the number tho. either way I am going to go normalize and see how it comes out thanks again....
|
Tags
|
1084, 440c, bee, billet, blade, carbon, damascus, drill, file, forge, heat, heat treat, knife, made, make, pattern, problem, small, steel, tang, welding |
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Thread Tools |
|
Display Modes |
Linear Mode
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is On
|
|
|
Similar Threads
|
Thread |
Thread Starter |
Forum |
Replies |
Last Post |
15n20
|
boatbuilder |
General ::: Items and Bargains |
3 |
01-01-2013 05:10 PM |
A?o 15N20
|
Thubalkain |
SBC Forum (Sociedade Brasileira de Cuteleiros) |
0 |
04-22-2008 11:55 AM |
15N20 or ?
|
BrianT |
Ed Caffrey's Workshop |
3 |
04-20-2004 06:15 PM |
15n20 And L6
|
bulldogsblades |
General ::: Items and Bargains |
3 |
01-01-2004 03:25 PM |
15n20 or L6
|
Squarenutt |
The Supply Center |
4 |
09-08-2001 12:50 AM |
All times are GMT -5. The time now is 09:32 PM.
|