The tin is vertical and the ends are open. Yes, the interrupted quench followed by pp gives noticeably better results on some steels like S30V. However, I wouldn't use that process unless the spec sheet suggests it.
I think you said you had some S35VN. You'll want that process for this steel if you want the best possible performance from it ...
|