Overheating...I didn't think about that, but I guess my forge is working well!
I will play with it more and see if I can get the process worked out better.
I do realize that some other steels are probably easier to learn on, but I trust the pedigree on this L6, but I didn't read up on it too much before I tried it.
Thank you both for your replies- very helpful information, and it is always great to learn fro others that have been down this road before!
I'll let you know how the next ones turn out, and I will try to normalize these again too.
Thanks again,
DJ
|