QUOTE: I don't know if 3 heating/quenching cycles would have caused deeper decarb or not.
I would certainly think it would increase your opportunity for decarb. I don't do any grinding until the HT is complete. That way, I know I got rid of any possible decarb and it reduces the chances of warping too ...
|