Ok see I am notorious for trying to many things at one (ray can verify that! LOL) but ray and ed are right usually when I do that I end up kicking myself in the butt....if you have a slight warp you can get it out in grinding.....when you buy steel its not perfect but if there is a warp its usually slight if its bad enough that you cant grind it out easily most likely you put that warp there one way or another.....also as ray said I follow the same thing I always cut the profile then heat treat then do the bevels I have done tons of blades this way probilly 95% of all the blades I have done...
|