Thanks again for the help, guys. Its hugely appreciated. Is steel i get from Aldo likely to be spheroidized? (thanks for explaining this term. I had no idea what people were talking about before) If i want to normalize it, what kind of a normalization cycle should I be shooting for and how much should I be worried about target temps for that? If i decided to get a pyrometer or make one, where in the forge should I be temping and how can I guarantee that I am hitting that temp in the blade metal?
|