so my trip back to mass. got delayed till tomorow so i was playing around with different etch times and dilutions on that piece of damascus....its showing up but it doesnt have a lot of contrast to it its like one step up from a hologram where you can only see it at certain angles is there any way to get more contrast to it or is that just how the 1084 and 15n20 mix comes out....when i HT it it should be done just how i do my plain 1084 right? maybe normalize or anneal first?....
|