I don't know why your blade is softer than expected but I do know that you can expect that the tang may not be as much softer as you hoped (assuming you get a successfully hardened blade eventually). The reason is that 440C is quite capable of hardening in still air, not quite as much as in oil but close, so that the tang seems likely to harden anyway ...
|