Hi guys
I just got a hold of this beauty:
Its 0,12" thick and 25" in diameter.
There are no marking on the blade and its possible to file it down.
How should i go about using this steel? Should i anneal if first before working it?
Should i HT as "normal" 3 normalization cycles and then try to see which hardness I get when quenchin around nonmagnetic?