Don't think you can get there from here
Maybe I am misunderstanding you but if you are trying to get your grid line flat like the first drawing, the tip will never be sharp. It will be at whatever thicknesses the steel is at the top of your grind. Picture a cross section of the grind the out to the tip.
|