Yes even with stainless in foil it will discolor and you will have to finish again...another problem if you do the bevels and thin the edge there is a very good chance that edge will warp back and forth and look a lil like bacon....yeh if you plate quench the plates push down on the blade but only on the flats so your spine wont bend and warp but if the bevels are done the plates don't actually touch them....just making double work for your self....I work with stainless more than anything else I will profile then HT before I even put in the bevels after its HT ed I will go back do the bevels and finish work....oh if you do the bevels and plate quench the plates as I said wont touch the bevels and wont suck out the heat as fast if you HT before it has bevels the plates touch the entire knife and you wont have that problem either