Old 07-15-2017, 11:10 PM
jimmontg jimmontg is offline
Guru
 
Join Date: Jan 2016
Location: Now live in Las Cruces NM.
Posts: 1,345
SteelP

I have no qualms whatsoever about using O1 in a forge. Can you bring out the best it has to offer? NO and you can't with any other steel either in a forge.(what's the temp?) Personally I think O1 is quite forgeable and the sweet spot HT temp is 1475. It should be held there for 10-15 minutes, but you do not have a HT oven. Forge will have to do. O1 is as good as 1084 in a forge. I use 1084 hardly at all, but I do use O1. Learn your temperature colors and read up on O1. I was a heat treater at a machinist shop and am very familiar with 1475 degree temp and color, O1 is resistant to being overheated, but will over heat so be careful. It is superior to 1084.


__________________
Now it says Guru and it used to say Master. I think I like Master better, though skilled would be the best description