Quote:
Originally Posted by jimmontg
Don't be sorry, you have to learn, but using mystery steels will give you some mystery results.lol
If you insist on using odd steels remember if it has been hardened before then it's OK to forge like mower blades, but some leaf springs may not work out as well as some of the newer ones aren't that great. Always take a small piece and heat to orangish red and quench. See how hard it is. Run a file across it, if it skips then temper at 400 for an hour and do what I said before. Buying some 1084 is a better idea though.
|
Ya it is time for me to get some of that, it is gonna be awhile since the move and all the other hassle around what happened. Then ill get a better job and start doing a lot more of this